PU varnish
Polyurethane colourless varnish for floor finishing. Two-component colourless polyurethane resin for floor protection. It is used in all flooring systems. The product is easy to apply, it is applied to the floor surface with a short-haired roller. The product has high chemical and mechanical resistance, also giving the floor resistance to UV radiation.
Characteristic
- low viscosity
- satin or matte floor finish
- UV resistant
- high chemical and mechanical resistance
- easy to use
- Easy to keep clean
Product purpose
- Matte or satin floor finish
- UV protection.
- For coatings made using painting and pouring techniques, with natural and colored quartz sand, as well as with a sprinkle of colored flakes.
- Widely used in apartments, industrial facilities, warehouses, parking lots and technical rooms, public utility buildings.
PRODUCT APPLICATION CONDITIONS:
AMBIENT TEMPERATURE: min. 10°C max. 30°C
Concrete TEMPERATURE: min. 10°C and min. 3°C above the dew point temperature
AIR HUMIDITY: max. 75%
MIESZANIE :
Materiały przeznaczone do użycia powinny mieć temperaturę min. 15 st. C.
Pour the entire contents of the component B package into the component A package.
Mix with a low-speed mixer for approximately 3 minutes (to avoid aeration of the material, it is recommended to use a mixer with a speed of approximately 300 rpm). The material should be poured into a clean container and mixed again for approximately 2 minutes. Due to the chemical reaction taking place, the material should be applied immediately after mixing. Do not leave the mixed material in the bucket.
USEFULNESS OF THE MIXTURE AT TEMPERATURE 20°C: 20–25 min.
USEFULNESS OF THE MIXTURE AT TEMPERATURE 30°C: 10–15 min.
Zużycie: ok. 0,2-0,25 kg/m2, przy dwóch zalecanych warstwach.
- Store in well-closed barrels or buckets
- keep open flames away
- minimum storage temperature +10°C
- do not allow contact with skin
- avoid inhaling material vapors
- do not allow individual components to come into contact with acids, strong oxidants, or bases
- the material does not pose a risk of spontaneous explosion